Silicone rubber for trademark

Silicone rubber for trademark
Silicone rubber for trademarkSilicone rubber for trademarkSilicone rubber for trademarkSilicone rubber for trademarkSilicone rubber for trademark
FOB Price

US $10.89200 - 500 kilogram

group name
silicone rubber for textile coating&trademakrs
Min Order
200 kilogram
brand name
Hong Ye silicone rubber
model
HY-966 silicon rubber
Nearest port for product export
Shenzhen, Guangzhou, xiamen, Shanghai
Delivery clauses under the trade mode
FOB, CFR, CIF, EXW
Acceptable payment methods
T/T, L/C, Westem Union
Export mode
Export through agents
update time
Fri, 25 Nov 2016 10:10:45 GMT

Paramtents

  • color clear

  • mix ratio 1:1 or10:1

  • HS code 39100000

  • application mold making

  • place China

  • sample available

  • delivery with 3 days

  • shelf life 12 month

  • MOQ 200kg

  • feature liquid

Packging & Delivery

  • Min Order200 kilogram

Briefing

The material can be fabricated into trademarks independently and through cloth pressing and leat

Detailed

The series of silicone rubber is divided into dispensing type HY-966 and  coating type HY-967. They can not only be fabricated into trademarks independently, but also be fabricated into trademarks through cloth pressing and leather pressing.

HY-966A/HY-966B dispensing type trademark silicone rubber belongs to liquid addition cure system. The amount of the curing agent can be 10% and can also be adjusted to the mixing proportion of 1 : 1. The curing agent is two-component high-strength liquid silicone rubber made of basic compound, cross-linking agent, catalyst, padding and additive. Those materials do not contain heavy metal and aroma solvent, hence, it's not harmful to human body.

Silicone rubber for trademark Standard Datasheet:

Item no.
HY-966
HY-967
Component
A
B
A
B
Appearance
Transparent
Transparent
Transparent
Transparent
Mix ratio   (%)
10
1
10
1
Viscosity (cps)
≥40000
≥35000
Pot life  (H)
1-1.5
1-1.5
Curing time (H)
12-16
12-16
Elongation (%)
≥400
≥400
Tear strength (KN/m)
≥15
≥20
Hardness  (A°)
Hardness can be adjusted according to the requirements of customers (20-28 A°)

Typical curing Condition:170℃×5mins, prolong or shorten the curing time appropriately according to the thickness and size of the product during actual use.

Silicone rubber for trademark Using Instructions: The mixing proportion of HY-966A and HY-966B is 10:1. Mix component A and component B sufficiently and evenly according to the mixing proportion before use. The process of vacuum-pumping is also needed.

Silicone rubber for trademark Note: The series of products must not be in contact with organisms like N, P, S, etc., ionic compounds like Hg, Bi, As, etc., and alkynes, vinyl compounds, etc. to avoid the situation at the products can not be cured due to platinum catalyst poisoning. The products particularly can not be in contact with PVC which contains lead causing catalyst poisoning. Some organic pigment also can slow down the curing time or cause uncured .


After HY-966A and HY-966B are mixed, the silicone rubber must be used up within 4 hours, otherwise the cross-linking and curing arises to lose effectiveness. In case of a higher surrounding temperature, more attention should be paid.
Silicone rubber for trademark Instruction: Typical data can not be directly used for actual production guidance. Please contact us for details.


Silicone rubber for trademark Package:General packages of HY-966 and HY-967 products is in 5kg per can, 20kg per pail and 200kg per barrel.


Silicone rubber for trademark Precautions: The products can be transported as safety and non-hazardous goods since they are noninflammable with resistance to a high temperature above 300℃.



Call Us Anytime With Questions About Your Application.

More information , pls feel free to contact Mr Johnson:

Tel:  (00) 86-755-89948006

Email: hyjljx(at)szrl(dot)net

Mobile :86-18938867605